ESAB OK Tigrod 12.64 TIG welding rod, G4Si1 / ER70S-6, Ø 2.0 x 1,000 mm, 5 kg, 126420R150
€36.80
Delivery time: 3-10 working days
- TIG solid rod G4Si1 / ER70S-6, copper-clad
- Diameter 2.0 mm, length 1,000 mm, 5 kg pack
- For unalloyed and low-alloy steels, fine-grained steels and pressure vessel steels
- EN ISO 636-A W 4Si1, weld metal W 46 5 4Si1, AWS A5.18 ER70S-6
- Notched impact energy 150 J at -40 °C
- Argon (I1) as shielding gas
- Approvals depending on the manufacturing site, including DB, VdTÜV and BV
Product information "ESAB OK Tigrod 12.64 TIG welding rod, G4Si1 / ER70S-6, Ø 2.0 x 1,000 mm, 5 kg, 126420R150"
126420R150 is the OK Tigrod 12.64 with a diameter of 2.0 mm. The rods are 1,000 mm long and come in packs of 5 kg. This filler metal belongs to the carbon-manganese steel group and is used for TIG welding of unalloyed and low-alloy steels. It is also available in thinner 1.6 mm versions, and thicker 2.4 mm and 3.2 mm versions.
Which steels are suitable
The rod is intended for root and joint welds on unalloyed and low-alloy steels. These include general-purpose structural steels, fine-grained structural steels and pressure vessel steels. ESAB cites grades ranging from P235/S235 to P460/S460 as examples, with suitability tested down to -40 °C.
Typical applications
- Root welds on unalloyed and low-alloy steels
- Joint welds on general structural steels and fine-grained structural steels
- Welds on pressure vessel steels with requirements down to -40 °C
Whether 2.0 mm is the suitable diameter depends on the weld geometry and the current at the welding machine. Anyone wishing to carry out the same task with a different diameter will find the relevant series numbers in the table.
| 1.6 mm | 126416R150 |
| 2.0 mm (this variant) | 126420R150 |
| 2.4 mm | 126424R150 |
| 3.2 mm | 126432R150 |
Approvals and classification
According to EN ISO 636-A, the wire is designated W 4Si1 and the weld metal W 46 5 4Si1. The AWS designation according to SFA A5.18 is ER70S-6. The following approvals are listed, depending on the plant location: ABS 3Y (I1), BV 3YM, CE EN 13479, DB 42.039.48, DNV-GL III YM (I1), LR 3Y H15 (I1), UKCA EN 13479 and VdTÜV 05260.
Mechanical properties
According to EN, the untreated weld metal has a yield strength of 525 MPa, a tensile strength of 595 MPa and an elongation at break of 26 %. The notched impact energy is 150 J (-40 °C) and 90 J (-50 °C). According to AWS testing, the values are 510 MPa, 610 MPa and 30 %. Welding is carried out using argon (I1, EN ISO 14175).
Technical details
| Diameter | 2.0 mm |
| Rod length | 1,000 mm |
| Pack size | 5 kg |
| Wire type | Copper-clad TIG rod, G4Si1 / ER70S-6 |
| Alloy type | Carbon-manganese steel |
| Shielding gas | I1 (argon, EN ISO 14175) |
| Wire classification | EN ISO 636-A: W 4Si1; SFA/AWS A5.18: ER70S-6 |
| Weld metal classification | EN ISO 636-A: W 46 5 4Si1 |
| Yield strength / Tensile strength / Elongation at break (EN) | 525 MPa / 595 MPa / 26 % |
| Yield strength / Tensile strength / Elongation at break (AWS) | 510 MPa / 610 MPa / 30 % |
| Notched impact energy (EN) | 150 J at -40 °C; 90 J at -50 °C |
| Wire composition C / Mn / Si | 0.074 / 1.68 / 0.95 % |
| Weld metal C / Mn / Si / S / P | 0.08 / 1.28 / 0.80 / 0.013 / 0.015 % |
Scope of delivery
- 1 pack of OK Tigrod 12.64, 5 kg, rods Ø 2.0 mm, length 1,000 mm